Copper(I) phosphide
| 200px | |
| Names | |
|---|---|
| IUPAC name
copper(I) phosphide
|
|
| Other names
copper phosphide, cuprous phosphide
|
|
| Identifiers | |
12019-57-7  |
|
| PubChem | 159399 |
| Properties | |
| Cu3P | |
| Molar mass | 221.6127 g/mol |
| Appearance | yellowish grey crystals |
| Melting point | 900 °C (1,650 °F; 1,170 K) |
| Structure | |
| Hexagonal, hP24 | |
| P63cm, No. 185 | |
| Vapor pressure | {{{value}}} |
|
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
|
|
 verify (what is  ?) |
|
| Infobox references | |
Copper phosphide, Cu3P, also copper(I) phosphide, cuprous phosphide, cuprophosphorus and phosphor copper, is a compound of copper and phosphorus, a phosphide of copper. It has the appearance of yellowish-grey very brittle mass of crystalline structure. It does not react with water.
Copper phosphide has a role in copper alloys, namely in phosphor bronze. It is a very good deoxidizer of copper.
Copper phosphide can be produced in a reverberatory furnace or in a crucible, e.g. by a reaction of red phosphorus with a copper-rich material. It can also be prepared photochemically, by irradiating cupric hypophosphite with ultraviolet radiation.[1]
When subjected to ultraviolet light, copper phosphide shows fluorescence.
A blue-black film of copper phosphide forms on white phosphorus when subjected to a solution of copper salt; wounds containing particles of phosphorus therefore have to be washed with 1% solution of copper sulfate. The particles then can be easily removed, which is helped by their fluorescence. Formation of protective layer of copper phosphide is also used in cases of phosphorus ingestion, when gastric lavage with copper sulfate is employed as part of the cure.[2]