Molybdenum disilicide

From Infogalactic: the planetary knowledge core
Jump to: navigation, search
Molybdenum disilicide
200px
Names
IUPAC name
Molybdenum disilicide
Identifiers
12136-78-6 YesY
PubChem 6336985
Properties
MoSi2
Molar mass 152.11 g/mol
Appearance gray metallic solid
Density 6.26 g/cm3[1][2]
Melting point 2,030 °C (3,690 °F; 2,300 K)[2]
Structure
Tetragonal[1]
I4/mmm (No. 139), tI6
a = 0.32112 nm, c = 0.7845 nm
Vapor pressure {{{value}}}
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
YesY verify (what is YesYN ?)
Infobox references

Molybdenum disilicide (MoSi2, or molybdenum silicide), an intermetallic compound, a silicide of molybdenum, is a refractory ceramic with primary use in heating elements. It has moderate density, melting point 2030 °C, and is electrically conductive. At high temperatures it forms a passivation layer of silicon dioxide, protecting it from further oxidation. It is a gray metallic-looking material with tetragonal crystal structure (alpha-modification); its beta-modification is hexagonal and unstable.[3] It is insoluble in most acids but soluble in nitric acid and hydrofluoric acid.

While MoSi2 has excellent resistance to oxidation and high Young's modulus at temperatures above 1000 °C, it is brittle in lower temperatures. Also, at above 1200 °C it loses creep resistance. These properties limits its use as a structural material, but may be offset by using it together with another material as a composite material.

Molybdenum disilicide and MoSi2-based materials are usually made by sintering. Plasma spraying can be used for producing its dense monolithic and composite forms; material produced this way may contain a proportion of β-MoSi2 due to its rapid cooling.

Molybdenum disilicide heating elements can be used for temperatures up to 1800 °C, in electric furnaces used in laboratory and production environment in production of glass, steel, electronics, ceramics, and in heat treatment of materials. While the elements are brittle, they can operate at high power without aging, and their electrical resistivity does not increase with operation time. Their maximum operating temperature has to be lowered in atmospheres with low oxygen content due to breakdown of the passivation layer.

Other ceramic materials used for heating elements are e.g. silicon carbide, barium titanate, and lead titanate composite materials.

Molybdenum disilicide is used in microelectronics as a contact material. It is often used as a shunt over polysilicon lines to increase their conductivity and increase signal speed.

References

  1. 1.0 1.1 Lua error in package.lua at line 80: module 'strict' not found.
  2. 2.0 2.1 Lua error in package.lua at line 80: module 'strict' not found.
  3. Lua error in package.lua at line 80: module 'strict' not found.