Tantalum pentoxide

From Infogalactic: the planetary knowledge core
Jump to: navigation, search
Tantalum pentoxide
200px
     Ta5+      O2−
Names
IUPAC name
Tantalum(V) oxide
Systematic IUPAC name
Ditantalum pentaoxide
Identifiers
1314-61-0 YesY
ChemSpider 452513 N
Jmol 3D model Interactive image
PubChem 518712
  • InChI=1S/5O.2Ta
  • O=[Ta](=O)O[Ta](=O)=O
Properties
Ta2O5
Molar mass 441.893 g/mol
Appearance white, odorless powder
Density β-Ta2O5 = 8.18 g/cm3[1]
α-Ta2O5 = 8.37 g/cm3
Melting point 1,872 °C (3,402 °F; 2,145 K)
negligible
Solubility insoluble in organic solvents and most mineral acids, reacts with HF
Band gap 3.8 - 5.3 eV
2.275
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
N verify (what is YesYN ?)
Infobox references

Tantalum pentoxide, also known as tantalum(V) oxide, is the inorganic compound with the formula Ta
2
O
5
. It is a white solid that is insoluble in all solvents but is attacked by strong bases and hydrofluoric acid. Ta
2
O
5
is an inert material with a high refractive index and low absorption (i.e. colourless), which makes it useful for coatings.[2] It is also extensively used in the production of capacitors, due to its high dielectric constant.

Preparation

Occurrence and Refining

Tantalum occurs in the minerals tantalite and columbite (columbium being an archaic name for niobium), which occur in pegmatites, an igneous rock formation. Mixtures of columbite and tantalite are called coltan. Tantalite was discovered by Anders Gustaf Ekeberg at Ytterby, Sweden, and Kimoto, Finland. The minerals microlite and pyrochlore contain approximately 70% and 10% Ta, respectively.

Tantalum ores often contain significant amounts of niobium, which is itself a valuable metal. As such, both metals are extracted so that they may be sold. The overall process is one of hydrometallurgy and begins with a leaching step; in which the ore is treated with hydrofluoric acid and sulfuric acid to produce water-soluble hydrogen fluorides, such as the heptafluorotantalate. This allows the metals to be separated from the various non-metallic impurities in the rock.

(FeMn)(NbTa)2O6 + 16 HF → H2[TaF7] + H2[NbOF5] + FeF2 + MnF2 + 6 H2O

The tantalum and niobium hydrogenflorides are then removed from the aqueous solution by liquid-liquid extraction using organic solvents, such as cyclohexanone or methyl isobutyl ketone. This step allows the simple removal of various metal impurities (e.g. iron and manganese) which remain in the aqueous phase in the form of fluorides. Separation of the tantalum and niobium is then achieved by pH adjustment. Niobium requires a higher level of acidity to remain soluble in the organic phase and can hence be selectively removed by extraction into less acidic water. The pure tantalum hydrogen fluoride solution is then neutralised with aqueous ammonia to give hydrated tantalum oxide (Ta2O5(H2O)x), which is calcinated to tantalum pentoxide (Ta2O5) as described in these idealized equations:[3]

H2[TaF7] + 5 H2O + 7 NH3 → 0.5 Ta2O5(H2O)5 + 7 NH4F
Ta2O5(H2O)5 → Ta2O5 + 5 H2O

From alkoxides

Tantalum oxide is frequently used in electronics, often in the form of thin films. For these applications it can be produced by MOCVD (or related techniques), which involves the hydrolysis of its volatile halides or alkoxides:

Ta2(OEt)10 + 5 H2O → Ta2O5 + 10 EtOH
2 TaCl5 + 5 H2O → Ta2O5 + 10 HCl

Structure and properties

The crystal structure of tantalum pentoxide has been the matter of some debate. The bulk material is disordered,[4] being either amorphous or polycrystalline; with single crystals being difficult to grow. As such Xray crystallography has largely been limited to powder diffraction, which provides less structural information.

At least 2 polymorphs are known to exist. A low temperature form, known as L- or β-Ta2O5, and the high temperature form known as H- or α-Ta2O5. The transition between these two forms is slow and reversible; taking place between 1000-1360 °C, with a mixture of structures existing at intermediate temperatures.[4] The structures of both polymorphs consist of chains built from octahedral TaO6 and pentagonal bipyramidal TaO7 polyhedra sharing opposite vertices; which are further joined by edge-sharing.[5][6] The overall crystal system is orthorhombic in both cases, with the space group of β-Ta2O5 being identified as Pna2 by single crystal X-ray diffraction.[7] A high pressure form (Z-Ta2O5) has also been reported, in which the Ta atoms adopt a 7 coordinate geometry to give a monoclinic structure (space group C2).[8]

The difficulty in forming material with a uniform structure has led to variations in its reported properties. Like many metal oxides Ta2O5 is an insulator and its band gap has variously been reported as being between 3.8 to 5.3 eV, depending on the method of manufacture.[9][10][11] In general the more amorphous the material the greater its observed band gap. It should be noted that these observed values are significantly higher than those predicted by computational chemistry (2.3 - 3.8 eV).[12][13][14]

Its dielectric constant is typically about ~25[15] although values of over 50 have been reported.[16] In general tantalum pentoxide is considered to be a high-k dielectric material.

Reactions

Ta2O5 does not react appreciably with either HCl or HBr, however it will dissolve in hydrofluoric acid, and reacts with potassium bifluoride and HF according to the following equation:[17][18]

Ta2O5 + 4 KHF2 + 6 HF → 2 K4[TaF7] + 5 H2O

Ta2O5 can be reduced to metallic Ta via the use of metallic reductants such as calcium and aluminium.

Ta2O5 + 5 Ca → 2 Ta + 5 CaO
Several 10uF x 30VDC rated tantalum capacitors, solid-bodied epoxy-dipped type. Polarity is explicitly marked.

Uses

In electronics

Owing to its high band gap and dielectric constant, tantalum pentoxide has found a variety of uses in electronics, particularly in tantalum capacitors. These are used in automotive electronics, cell phones, and pagers, electronic circuitry; thin-film components; and high-speed tools. In the 1990s, interest grew in the use of tantalum oxide as a high-k dielectric for DRAM capacitor applications.,[19][20]

It is used in on-chip metal-insulator-metal capacitors for high frequency CMOS integrated circuits. Tantalum oxide may have applications as the charge trapping layer for Non-volatile memories.,[21][22] There are applications of tantalum oxide in resistive switching memories.[23]

Other uses

Due to its high refractive index, Ta2O5 has been utilized in the fabrication of the glass of photographic lenses.[2][24]

References

  1. Lua error in package.lua at line 80: module 'strict' not found.
  2. 2.0 2.1 Lua error in package.lua at line 80: module 'strict' not found.
  3. Lua error in package.lua at line 80: module 'strict' not found.
  4. 4.0 4.1 Lua error in package.lua at line 80: module 'strict' not found.
  5. Lua error in package.lua at line 80: module 'strict' not found.
  6. Lua error in package.lua at line 80: module 'strict' not found.
  7. Lua error in package.lua at line 80: module 'strict' not found.
  8. Lua error in package.lua at line 80: module 'strict' not found.
  9. Lua error in package.lua at line 80: module 'strict' not found.
  10. Lua error in package.lua at line 80: module 'strict' not found.
  11. Lua error in package.lua at line 80: module 'strict' not found.
  12. Lua error in package.lua at line 80: module 'strict' not found.
  13. Lua error in package.lua at line 80: module 'strict' not found.
  14. Lua error in package.lua at line 80: module 'strict' not found.
  15. Lua error in package.lua at line 80: module 'strict' not found.
  16. Lua error in package.lua at line 80: module 'strict' not found.
  17. Agulyansky, A. "Potassium fluorotantalate in solid, dissolved and molten conditions" J. Fluorine Chemistry 2003, 155-161. doi:10.1016/S0022-1139(03)00190-8
  18. Lua error in package.lua at line 80: module 'strict' not found.
  19. Lua error in package.lua at line 80: module 'strict' not found.
  20. Lua error in package.lua at line 80: module 'strict' not found.
  21. Lua error in package.lua at line 80: module 'strict' not found.
  22. Lua error in package.lua at line 80: module 'strict' not found.
  23. Lua error in package.lua at line 80: module 'strict' not found.
  24. Lua error in package.lua at line 80: module 'strict' not found.